Kimya PA6-CO Filament 3D

The Kimya PA6-CO filament is a co-polymer based on a Nylon 6 grade. This unfilled polyamide has excellent tensile strength and very low warping behavior. Unlike other polyamide filaments on the market the PA6-CO is very easy to print and can be used seamlessly on open chamber 3D printers. It is the perfect standard polyamide go-to thanks to its inherent polyamide properties of high mechanical, chemical and  heat resistance. Due to the general moisture sensitivity of polyamides, the filament must be dried before printing.

  • Excellent printability even on open chamber printers
  • Low warping
  • Good wear resistance

2-years KIMYA warranty.
Store away from light, humidity and heat to maintain the properties of the product.

Diameter : 1.75mm
Net Weight : 750g
Color : Black
Find your reseller
SKU: N/A GTIN: N/A
Product Dimensions: N/A; N/A Categories: , ,

FILAMENT PROPERTIES

PROPERTIES TEST METHODS VALUES
Diameter INS-6712 1.75 ± 0.1 mm
2.85 ± 0.1 mm
Density ISO 1183-1 1.157 g/cm3
Melt flow index (MFI) ISO 1133-1 (@240°C – 5 kg) 24 - 28 g/10min
Glass transition temperature (Tg) ISO 11357-1 DSC (10°C/min - 20-300°C) 65 °C
Melting Temperature (Tm) ISO 11357-1 DSC (10°C/min – 20-300°C) 227 °C

PRINT PARAMETERS AND SPECIMENS DIMENSIONS

PRINTING DIRECTION XY
Printing Speed 55 mm/s
Infill 100% - rectilinear
Infill Angle 45°/-45°
Nozzle Temperature 270°C
Bed T° 75°C

PRINTED SPECIMENS PROPERTIES

PROPERTIES TEST METHODS VALUES
MECHANICAL PROPERTIES Tensile modulus ISO 527-2/5A/50 2,166 MPa
Tensile Strength ISO 527-2/5A/50 56.1 MPa
Tensile strain at strength ISO 527-2/5A/50 4,3 %
Tensile Stress at Break ISO 527-2/5A/50 13.4 MPa
Tensile strain at break (type A) ISO 527-2/5A/50 16.2 %
Flexural modulus ISO 178 2,017 MPa
Deformation at Flexural Strain ISO 178 <5 %
Flexural stress at conventional deflection (3,5% strain)* ISO 178 65.9 MPa
Charpy impact resistance ISO 179-1/1eA 3.9 kJ/m²
Shore Hardness ISO 868 77,3

Revised on 16/06/2022.

Complete this form to download the technical product sheet : "Kimya PA6-CO Filament 3D"

Once the spool is dried, we recommend that it be used within 24 hours and maximum 7 days without drying.

We have carried out several printing tests on Kimya PA6-CO and recommend the following:

Extrusion temperature: 260 – 280°C
Plate temperature: 70 – 100°C
Printing speed: 40 – 70 mm/s

3D PRINTING PROFILES

3D Printer Last update Do you have a project ?
Ultimaker S3 07/07/2022 Contact Us
Ultimaker S5 07/07/2022 Contact Us

MISCELLANEOUS

CERTIFICATIONS AND USES

PROPERTIES RATING
Ease to print
Rigidity
Impact Strength
Sensitivity to moisture
Temperature resistance
Weather Resistance
RoHs Compliant
EU 10/2011 Non Compliant
FDA Non Compliant
UL94 - V0 Non Compliant
ESD Protection Non Compliant

Reviews

There are no reviews yet.

Be the first to review “Kimya PA6-CO Filament 3D”

Related products