Kimya HIPS-R 3D Filament

The Kimya HIPS-R 3D filament belongs to the styrenic polymer family. This High Impact PolyStyrene (HIPS) is a thermoplastic formulated from recycled materials and which –despite being recycled– boasts good resistance to impact and heat.  It is highly impermeable, enabling it to be used in container applications free of any leakage. HIPS-R has another property distinguishing it from all other filaments: its solubility in D-limonene. Indeed, it can be used as a supporting material.  It is used in the manufacture of packaging and also household appliances. The Kimya HIPS-R 3D filament has the following properties:

  • Good impact resistance
  • 100% made from recycled materials
  • Soluble in D-Limonene
  • Complies with REACH and RoHS standards

 

Diameter : 1.75mm
Net Weight : 500g
Color : Natural
Find your reseller
SKU: N/A GTIN: N/A Categories: , ,

FILAMENT PROPERTIES

PROPERTIES TEST METHODS VALUES
Diameter INS-6712 1.75 ± 0.1 mm
Density ISO 1183-1 1.03 g/cm3
Moisture rate INS-6711 < 1 %
Melt flow index (MFI) ISO 1133-1 (@200°C – 5 kg) 4.7 - 7.1 g/10min
Glass transition temperature (Tg) ISO 11357-1 DSC (10°C/min - 20-260°C) 97 °C

PRINT PARAMETERS AND SPECIMENS DIMENSIONS

PRINTING DIRECTION XY
Printing Speed 20-70 mm/s
Infill 100% - rectilinear
Infill Angle 45°/-45°
Nozzle Temperature 250-290°C
Bed T° 60-110°C

PRINTED SPECIMENS PROPERTIES

PROPERTIES TEST METHODS VALUES
MECHANICAL PROPERTIES Tensile modulus ISO 527-2/5A/50 1,273 MPa
Tensile Strength ISO 527-2/5A/50 23.7 MPa
Tensile strain at strength ISO 527-2/5A/50 1 %
Tensile Stress at Break ISO 527-2/5A/50 16.7 MPa
Tensile strain at break ISO 527-2/5A/50 11 %
Flexural modulus ISO 178 1,533 MPa
Flexural stress at conventional deflection (3,5% strain)* ISO 178 36.2 MPa
Charpy impact resistance ISO 179-1/1eA 7 kJ/m²
Shore Hardness ISO 868 76,6D
Note 1 *According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2 The data should be considered as indicative values - Properties can be influenced by production conditions.

Created on 18/12/2019 - Revised on 18/12/2019.

Complete this form to download the technical product sheet : "Kimya HIPS-R 3D Filament"

OUR TIPS FOR BETTER PRINTING

  • PRINT SPEED : 20-70 mm/s
  • EXTRUSION TEMPERATURE : 250-290°C
  • PLATFORM TEMPERATURE : 60-110°C

MISCELLANEOUS

Spool Material PS
Steaming Temperature 80°C
Steaming Duration 2h-4h

CERTIFICATIONS AND USES

PROPERTIES RATING
Ease to print
Rigidity
Impact Strength
Sensitivity to moisture
Temperature resistance
Weather Resistance
RoHs Non Compliant
EU 10/2011 Non Compliant
FDA Non Compliant
UL94 - V0 Non Compliant
ESD Protection Non Compliant

Reviews

There are no reviews yet.

Be the first to review “Kimya HIPS-R 3D Filament”

Your email address will not be published. Required fields are marked *