FILAMENT PROPERTIES
| PROPERTIES | TEST METHODS | VALUES |
|---|---|---|
| Diameter | INS-6712 |
1.75 ± 0.1 mm 2.85 ± 0.1 mm |
| Density | ISO 1183-1 | 1.037 g/cm3 |
| Moisture rate | INS-6711 | < 1 % |
| Melt flow index (MFI) | ISO 1133-1 (@220°C – 10 kg) | 14.8 g/10min |
| Glass transition temperature (Tg) | ISO 11357-1 DSC (10°C/min - 20-220°C) | 100 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION | XY |
|---|---|
| Printing Speed | 40-70 mm/s |
| Infill | 100% - rectilinear |
| Infill Angle | 45°/-45° |
| Nozzle Temperature | 250-270°C |
| Bed T° | 90-110°C |
PRINTED SPECIMENS PROPERTIES
| PROPERTIES | TEST METHODS | VALUES | |
|---|---|---|---|
| MECHANICAL PROPERTIES | Tensile modulus | ISO 527-2/5A/50 | 1,775 MPa |
| Tensile Strength | ISO 527-2/5A/50 | 31.1 MPa | |
| Tensile strain at strength | ISO 527-2/1A/50 | 2 % | |
| Tensile Stress at Break | ISO 527-2/5A/50 | 27.7 MPa | |
| Tensile strain at break | ISO 527-2/5A/50 | 4 % | |
| Flexural modulus | ISO 178 | 1,509 MPa | |
| Flexural strength* | ISO 178 | > 5 % | |
| Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 44.7 MPa | |
| Charpy impact resistance | ISO 179-1/1eA | 8 kJ/m² | |
| Shore Hardness | ISO 868 | 65,2D |
| Note 1 | *According to ISO 178, end of the test at 5% deformation even if there is no specimen break. |
| Note 2 | The data should be considered as indicative values - Properties can be influenced by production conditions. |
Created on 13/02/2018 - Revised on 01/07/2019.