Kimya PLA-R 3D Filament

The 3D filament Kimya PLA-R is a recycled and biodegradable polymer: this biosourced homopolymer can be obtained from corn starch. Polylactic acid (PLA) is a natural alternative to polyethylene. It is easy to print and is odorless. The 3D filament Kimya PLA-R can be used in industrial applications, notably packaging, and also in domestic applications:  creation of everyday objects, toys, prototypes and for use in modeling. It offers the following properties:

  • Easy to print
  • Odorless
  • Glossy finish
  • ≥ 97% recycled materials (100% recycled materials – PLA-R Natural)
  • Eligible to the EN 13432 and EN 14995 standards (PLA-R Natural)
  • Complies with the REACH standard

2-year ARMOR warranty.

Diameter : 1.75mm
Net Weight : 750g
Color : White
Find your reseller
SKU: N/A GTIN: N/A Categories: , , ,

FILAMENT PROPERTIES

PROPERTIES TEST METHODS VALUES
Diameter INS-6712 1.75 ± 0.1 mm
2.85 ± 0.1 mm
Density ISO 1183-1 1.24 g/cm3
Moisture rate INS-6711 < 1 %
Melt flow index (MFI) ISO 1133-1 (@210°C – 2,16 kg) 9 - 12 g/10min
Glass transition temperature (Tg) ISO 11357-1 DSC (10°C/min - 20-220°C) 61 °C
Melting Temperature (Tm) ISO 11357-1 DSC (10°C/min – 20-220°C) 150 °C

PRINT PARAMETERS AND SPECIMENS DIMENSIONS

PRINTING DIRECTION XY
Printing Speed 40-150 mm/s
Infill 100% - rectilinear
Infill Angle 45°/-45°
Nozzle Temperature 190-210°C
Bed T° 20-60°C

PRINTED SPECIMENS PROPERTIES

PROPERTIES TEST METHODS VALUES
MECHANICAL PROPERTIES Tensile modulus ISO 527-2/5A/50 2,963 MPa
Tensile Strength ISO 527-2/5A/50 57.9 MPa
Tensile strain at strength ISO 527-2/5A/50 2.2 %
Tensile Stress at Break ISO 527-2/5A/50 47.3 MPa
Tensile strain at break ISO 527-2/5A/50 4 %
Flexural modulus ISO 178 2,675 MPa
Flexural stress at conventional deflection (3,5% strain)* ISO 178 88.8 MPa
Flexural stress at break ISO 178 91.6 MPa
Charpy impact resistance ISO 179-1/1eA 3.22 kJ/m²
Shore Hardness ISO 868 79.1D
Note 1 *According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2 The data should be considered as indicative values - Properties can be influenced by production conditions.

Created on 07/01/2018 - Revised on 01/07/2019.

Complete this form to download the technical product sheet : "Kimya PLA-R 3D Filament"

PRINT SETTINGS:

  • PRINT SPEED : 40-150 mm/s
  • EXTRUSION TEMPERATURE : 190-210°C
  • PLATFORM TEMPERATURE : 20-60°C

Available printing setting:

3D PRINTING PROFILES

3D Printer Last update Do you have a project ?
Raise3D Pro2 20/02/2019 Contact Us
Ultimaker S5 15/07/2020 Contact Us
Volumic 20 Pro MK2 14/02/2019 Contact Us
Volumic 30 Pro 14/02/2019 Contact Us

MISCELLANEOUS

Spool Material PS
Steaming Temperature 65°C
Steaming Duration 2h-4h

Find more information about our Kimya PLA-R 3D filament:

CERTIFICATIONS AND USES

PROPERTIES RATING
Ease to print
Rigidity
Impact Strength
Sensitivity to moisture
Temperature resistance
Weather Resistance
RoHs Non Compliant
EU 10/2011 Non Compliant
FDA Non Compliant
UL94 - V0 Non Compliant
ESD Protection Non Compliant

Reviews

There are no reviews yet.

Be the first to review “Kimya PLA-R 3D Filament”