Kimya ABS-S 3D Filament

The 3D filament Kimya ABS-S belongs to the styrenic polymer family. Acrylonitrile butadiene styrene (ABS) is a thermoplastic polymer offering high impact resistance and is relatively rigid and lightweight. Due to its excellent surface appearance and decorative qualities (it can be easily colored), ABS is widely used in outer casing applications in sectors such as domestic appliances, telephony, IT equipment and toys.

  • Impact resistance
  • Higher heat resistance than PLA (around 90°C)
  • A filament that can be used in all 3D printers on the market
  • Large formats from 5kg to 10kg and different colors available on request
  • Food contact certified under EU 10/2011 and FDA 21 CFR (white only)
  • Complies with the RoHS and REACH standards

2-year ARMOR warranty.

Diameter : 1.75mm
Net Weight : 500g
Color : White
Find your reseller
SKU: N/A GTIN: N/A Categories: , ,

FILAMENT PROPERTIES

PROPERTIES TEST METHODS VALUES
Diameter INS-6712 1.75 ± 0.1 mm
2.85 ± 0.1 mm
Density ISO 1183-1 1.035 g/cm3
Moisture rate INS-6711 < 1 %
Melt flow index (MFI) ISO 1133-1 (@220°C – 10 kg) 3.5 - 6 g/10min
Glass transition temperature (Tg) ISO 11357-1 DSC (10°C/min - 20-300°C) 107 °C

PRINT PARAMETERS AND SPECIMENS DIMENSIONS

PRINTING DIRECTION XY
Printing Speed 20-60 mm/s
Infill 100% - rectilinear
Infill Angle 45°/-45°
Nozzle Temperature 250-270°C
Bed T° 85-100°C

PRINTED SPECIMENS PROPERTIES

PROPERTIES TEST METHODS VALUES
MECHANICAL PROPERTIES Tensile modulus ISO 527-2/5A/50 1,484 MPa
Tensile Strength ISO 527-2/5A/50 35.3 MPa
Tensile strain at strength ISO 527-2/5A/50 2.7 %
Tensile Stress at Break ISO 527-2/5A/50 22.8 MPa
Tensile strain at break ISO 527-2/5A/50 9.8 %
Flexural modulus ISO 178 1,443 MPa
Flexural strength* ISO 178 5 %
Flexural stress at conventional deflection (3,5% strain)* ISO 178 43.6 MPa
Charpy impact resistance ISO 179-1/1eA 24.7 kJ/m²
Shore Hardness ISO 868 70D
Note 1 *According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2 The data should be considered as indicative values - Properties can be influenced by production conditions.

Created on 25/11/2019 - Revised on 25/11/2019.

Complete this form to download the technical product sheet : "Kimya ABS-S 3D Filament"

PRINT SETTINGS:

  • PRINT SPEED : 20-60 mm/s
  • EXTRUSION TEMPERATURE : 250-270°C
  • PLATFORM TEMPERATURE : 85-100°C

MISCELLANEOUS

Spool Material PC
Steaming Temperature 80°C
Steaming Duration 2h-4h

CERTIFICATIONS AND USES

PROPERTIES RATING
Ease to print
Rigidity
Impact Strength
Sensitivity to moisture
Temperature resistance
Weather Resistance
RoHs Compliant
EU 10/2011 Compliant
FDA Compliant
UL94 - V0 Non Compliant
ESD Protection Non Compliant